Kent, don't you always get some excessive weld on the backside when using filler? Whether it's O/A or TIG? I always have. Fusion weld with steel using O/A, I don't get any.Slight undercut on the top but from what I've seen that's normal when fusion welding. Are we talking about two different things?
__________________
Chris (trying to be the best me I can be)
|