Default Welding aluminium

Yes I agree with most of that Andy, however I find small circular motion works for me,also I normally dress my welds after removing flux with hot water because a lot of the time i will not need to file it also it work hardens the weld and the surrounding material ,this helps when making large panels.
But at the end of the day it is all down to if it works for you then do what works .
I have been welding aluminium for about 40 years and I was taught by a 70 year old and I would think things have changed over the years,but I am to old to try new things now,and if you say to anyone that you only weld aluminium with gas they look at you as if you are mad,but I have tried tig a few years ago and yes it it welds aluminium sheet but the weld it to hard
Old man but still learning


Last edited by Dell; 01-29-2018 at 02:53 PM. Reason: Forgot something
Reply With Quote

Thread Tools Search this Thread
Search this Thread:

Advanced Search
Display Modes

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off

Forum Jump

All times are GMT -5. The time now is 01:44 PM.

Powered by vBulletin® Version 3.8.6
Copyright ©2000 - 2018, Jelsoft Enterprises Ltd.